Sefydlu Rhannau Dur Brazing i Plât Carbid Twngsten

Sefydlu Rhannau Dur Brazing i Plât Carbid Twngsten

Amcan
Bragu Sefydlu Rhannau Dur i Plât Carbid Twngsten

offer

Peiriant bresyddu ymsefydlu llaw DW-UHF-6KW-III

Sefydlu dur dur pres

Prawf 1

deunyddiau
• Gwialen ddur: 19.05 mm (0.75 ″) OD, 82.55 mm (3.25 ″) Hyd

• Plât Carbid Twngsten: 38.1 mm (1.5 ″) OD, 10.16 mm (0.4 ″) Trwch

• Alloy: 19.05 mm (0.75 ″) Disgiau pres

Power: 4.0 kW
Tymheredd: Tua 760 ° C (1400 ° F)
Amser: 40 sec

Prawf 2

deunyddiau
• Gwialen ddur: 12.7 mm (0.50 ″) OD, 76.2 mm (3 ″) Hyd

• Plât Carbid Twngsten: 19.05 mm (0.75 ″) OD, 6.35 mm (0.25 ″) Trwch

• Alloy: 12.7 mm (0.50 ″) Disgiau pres

Power: 2.36 kW
Tymheredd: Tua 760 ° C (1400 ° F)
Amser: 23 sec

Prawf 3

deunyddiau
• Gwialen ddur: 12.7 mm (0.50 ″) OD, 76.2 mm (3 ″) Hyd

• Plât Carbid Twngsten: 1 ″ OD, 1.39mm (0.055 ″) Trwch

• Alloy: 12.7 mm (0.50 ″) Disgiau pres

Power: 2.36 kW
Tymheredd: Tua 760 ° C (1400 ° F)
Amser: 20-25 eiliad (Pylsio ymlaen / i ffwrdd)

Prawf 4

deunyddiau
• Gwialen ddur: 6.35 mm (0.25 ″) OD, 76.2 mm (3 ″) Hyd

• Plât Carbid Twngsten: 21.08mm (0.83 ″) OD, 1.65mm (0.065 ″) thicknes

• Alloy: 6.35 mm (0.25 ″) Disgiau pres

Power: 1.96 kW
Tymheredd: Tua 760 ° C (1400 ° F)Sefydlu carbide dur brazingSefydlu dur dur presSefydlu dur dur pres
Amser: 20 eiliad (Pylsio ymlaen / i ffwrdd)

Canlyniadau a Chasgliadau:

Mae'n bosibl presio gwahanol rannau dur i ddisgiau carbid gydag un coil sefydlu. Roedd pŵer yn cael ei reoleiddio trwy droi'r gwres ymlaen ac i ffwrdd gan ddefnyddio switsh troed i atal gorgynhesu'r rhannau carbid.

 

=